Description
Atlas is used for: final cementation of implant prosthesis, crowns, bridges, in-lays, on-lays, Maryland bridges, veneers, cementation of posts and pins, pit and fissure sealants, periodontal splinting, and cementation of orthodontic bands and appliances.
Outstanding Features of Material
Fluoride release
X-ray opacity
Excellent handling characteristics
Low irritation potential
Negligible solubility
Low film thickness
Excellent resistance to oral environment and mechanical strength assure good long-term performance
Long shelf-life
Specifications
Typical Composition | Working Properties | Physical Properties |
|---|---|---|
Resin based BIS-GMA, radio opaqueglass filler, pyrogenic silica, catalyst,stabilizers, and pigments | Mixing time-Auto-Mix S-m. | Barcol hardness- 70 |
Total filler content (by weight)-61% | Working time (incl. mixing time; (23 °C); 74°F-> 90 sec | Color stability- very good |
Total filler content (by volume)-41% | Depth of light cure-> 1,75 mm* | Compressive strength- 55 MPa |
Specific gravity-1.72 g/cm3 | Self-cured mode (37 °C); 99 °F;-3:00 min | Diametral tensile strength- 52 MPa |
Flexual modules- 5000 MPa | ||
Flexural (transverse) strength- 130 Mpa | ||
Radio opacity- ca.250% Al | ||
Water solubility- <5 µg/mm3 | ||
Water sorption- <20 µg/mm3 |