Description
Regular Eagle Kit
All Natural Eagle Kit
All Contrast Eagle Kit
*Eagle-Light, Self & Dual-Cure Core Build-Up Material In dual cure mode restorative pastes are mixed with accelerators, this permits complete set of the material irrespective of the thickness of the restoration, or the accessibility of light.
*Virtually unlimited working time in light-cure mode; convenient working time in self-cure mode.
*Well-balanced x-ray opacity permits easy distinguishing from tooth structure, pins and posts.
*Moldable, non sticky consistency.
*Allows one to control consistency, whenever desirable, by adding either liquid or paste-type catalyst for dual cure.
*Contains moderately hard filler for easier carving and shaping.
*Does not require refrigeration: long shelf life at ambient temperatures.
*The Standard Eagle kit contains two shades: contrasting for easy distinguishing from tooth structure; and the natural for use under semi-transparent ceramics.
Instructions & MSDS
Comparison of Properties of Cured Eagle Core Build-Up Material with Glass Ionomer Cements, and with the Requirements of ADA Specification No.27 for Composite Restoratives
Regular Eagle Kit
All Natural Eagle Kit
All Contrast Eagle Kit
*Virtually unlimited working time in light-cure mode; convenient working time in self-cure mode.
*Well-balanced x-ray opacity permits easy distinguishing from tooth structure, pins and posts.
*Moldable, non sticky consistency.
*Allows one to control consistency, whenever desirable, by adding either liquid or paste-type catalyst for dual cure.
*Contains moderately hard filler for easier carving and shaping.
*Does not require refrigeration: long shelf life at ambient temperatures.
*The Standard Eagle kit contains two shades: contrasting for easy distinguishing from tooth structure; and the natural for use under semi-transparent ceramics.
Property | Eagle Core Build-up Material | Type I | Type II | Glass Ionomer |
|---|---|---|---|---|
Compressive Strength | 30761.2 psi (212 MPa) | not specified | not specified | 14.500-2.500 psi (100-190 MPa) |
Diametral Tensile Strength | 6384.4 psi (45 MPa) | 3480 psi (24MPa) | 4930 psi (34MPa) | 1300-2170 psi (9-15 MPa) |
Hardness (Barcol) | 70 | not specified | not specified | 75-86 |
Solubility in Water | virtually insoluble | not specified | not specified | 0.1 -2.0% |
Working Time (at 23ºC in self-cure mode) | 135 seconds | min. 90 seconds | min. 90 seconds | 120-240 seconds |
Setting Time (at 23ºC in self-cure mode) | 240 seconds | max. 8 mm. | max. 8 mm. | 7-15 min. |